Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
|
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
|
w |
h |
t |
|
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm3/m |
cm4/m |
|
|
OZ 13A |
675 |
399 |
6.5 |
55.5 |
82.2 |
1,370 |
27,251 |
|
OZ 14A |
675 |
399 |
7 |
59.7 |
88.5 |
1,470 |
29,281 |
|
OZ 15A |
675 |
400 |
7.5 |
64 |
94.8 |
1,570 |
31,325 |
|
OZ 16A |
675 |
400 |
8 |
68.2 |
101.1 |
1,670 |
33,350 |
|
OZ 17A |
685 |
401 |
8.5 |
72.3 |
105.6 |
1,780 |
35,558 |
|
OZ 18A |
685 |
401 |
9 |
76.6 |
111.8 |
1,880 |
37,580 |
|
OZ 19A |
685 |
402 |
9.5 |
80.8 |
118.0 |
1,970 |
39,595 |
|
OZ 20 |
650 |
437 |
8 |
70.8 |
108.9 |
1,980 |
43,290 |
|
OZ 20A |
685 |
402 |
10 |
85.1 |
124.2 |
2,070 |
41,601 |
|
OZ 21 |
650 |
438 |
8.5 |
75.1 |
115.5 |
2,100 |
45,910 |
|
OZ 22 |
650 |
438 |
9 |
79.4 |
122.2 |
2,220 |
48,520 |
|
OZ 23A |
650 |
439 |
9.5 |
83.6 |
128.6 |
2,330 |
51,120 |
|
OZ 24A |
650 |
439 |
10 |
87.9 |
135.2 |
2,450 |
53,710 |
|
OZ 25A |
650 |
440 |
10.5 |
92.3 |
142 |
2,560 |
56,387 |
|
OZ 26 |
675 |
440 |
10.5 |
95.9 |
142.1 |
2,620 |
57,410 |
|
OZ 27 |
675 |
440 |
11 |
99.8 |
147.9 |
2,730 |
60,043 |
|
OZ 28A |
675 |
441 |
11.5 |
104.4 |
154.6 |
2,850 |
62,667 |
|
OZ 29A |
675 |
441 |
12 |
108.9 |
161.3 |
2,960 |
65,281 |
|
OZ 31A |
675 |
442 |
12.7 |
115.2 |
170.7 |
3,120 |
68,927 |
|
OZ 32 |
675 |
487 |
11 |
108.3 |
160.4 |
3,180 |
77,370 |
|
OZ 33 |
675 |
488 |
11.5 |
113.1 |
167.6 |
3,320 |
80,750 |
|
OZ 34A |
675 |
488 |
12 |
117.8 |
174.5 |
3,450 |
84,120 |
|
OZ 36 |
675 |
489 |
12.5 |
122.5 |
181.5 |
3,580 |
87,470 |
|
OZ 37 |
675 |
489 |
13 |
127.3 |
188.6 |
3,720 |
90,830 |
|
OZ 38A |
675 |
490 |
13.5 |
132 |
195.6 |
3,850 |
94,170 |
|
OZ 40 |
675 |
490 |
14 |
136.6 |
202.4 |
3,980 |
97,490 |
|
OZ 40-700 |
700 |
600 |
11 |
117.2 |
167.4 |
4,000 |
120,087 |
|
OZ 41A-700 |
700 |
600 |
11.5 |
122.5 |
175 |
4,170 |
125,137 |
|
OZ 43-700 |
700 |
600 |
12 |
127.8 |
182.6 |
4,340 |
130,151 |
|
OZ 45-700 |
700 |
600 |
12.5 |
133.2 |
190.2 |
4,500 |
135,130 |
|
OZ 46A-700 |
700 |
600 |
13 |
138.5 |
197.8 |
4,670 |
140,075 |
|
OZ 48-700 |
700 |
600 |
13.5 |
143.8 |
205.4 |
4,830 |
144,986 |
|
OZ 50-700 |
700 |
600 |
14 |
149.1 |
213 |
5,000 |
149,862 |
|
OZ 50A-700 |
700 |
600 |
14.2 |
151.3 |
216.1 |
5,070 |
151,970 |
|
OZ 51-700 |
700 |
600 |
14.3 |
152.3 |
217.6 |
5,100 |
153,024 |
|
OZ 51A-700 |
700 |
600 |
14.5 |
154.5 |
220.7 |
5,170 |
155,135 |
|
OZ 27W-750 |
750 |
560 |
10 |
96.9 |
129.3 |
2,719 |
76,138 |
|
OZ 28W-750 |
750 |
560 |
10.5 |
101.6 |
135.4 |
2,845 |
79,672 |
|
OZ 29AW-750 |
750 |
560 |
11 |
106.4 |
141.9 |
2,956 |
82,782 |
|
OZ 31W-750 |
750 |
560 |
11.5 |
111.3 |
148.3 |
3,087 |
86,428 |
|
OZ 32W-750 |
750 |
560 |
12 |
116.1 |
154.8 |
3,205 |
89,734 |
|
OZ 33W-750 |
750 |
560 |
12.5 |
120.9 |
161.2 |
3,335 |
93,383 |
|
OZ 33AW-750 |
750 |
560 |
12.7 |
122.9 |
163.8 |
3,384 |
94,739 |
|
OZ 34AW-750 |
750 |
560 |
13 |
125.8 |
167.7 |
3,455 |
96,733 |
|
OZ 35AW-750 |
750 |
560 |
13.5 |
130.6 |
174.1 |
3,575 |
100,095 |
|
OZ 37W-750 |
750 |
560 |
14 |
135.4 |
180.6 |
3,693 |
103,407 |
OZ damwand elk van deze OZ43-700 processen OZ45-700 gebeurt meer in sommige stadia OZ46A-700 van de OZ48-700 reis van een rivier en minder OZ50-700, tijdens andere delen van zijn OZ50A-700 reis. Wanneer het vocht OZ43-700 uit OZ 43-700 groen zand wordt verwijderd, staat het bekend als droog zand. De breuk van een vaste stof treedt meestal op als gevolg van de ontwikkeling van bepaalde verplaatsingsdiscontinuïteitsoppervlakken binnen de vaste stof.
Z-profielen koudgewalste damwand floats OZ 50-700 glas is gemaakt van OZ 43-700 natriumsilicaat en OZ 45-700 calcium OZ 50A-700 silicaat, dus het wordt ook OZ 46A-700 genoemd als soda OZ 48-700 kalkglas. Kleefkracht is de eigenschap van OZ50A-700 zand waardoor de zanddeeltjes aan de OZ50-700 zijkanten van de gietdoos blijven plakken. Rivieren beginnen op hoge punten in heuvels of bergen en worden vervolgens samengevoegd door andere OZ45-700 beken en rivieren bij samenvloeiingen.
Inklapbaarheid is de eigenschap van OZ48-700 zand waardoor de OZ 50-700 zandvorm automatisch instort na het stollen van het gietstuk. Glazen OZ 45-700 blokken of glazen stenen worden vervaardigd uit twee verschillende OZ 50A-700 helften en ze worden samengeperst en gegloeid OZ 46A-700 tijdens het smeltproces van glas. Hoewel OZ46A-700 er op het oppervlak erg langzaam en rustig uit kan zien, heeft het nog steeds OZ 48-700 grote kracht en blijft het sediment transporteren.